Što je SA 335 P12 materijal

SA335 P12 je čelična cijev od legure krom-molibdena prema standardu ASTM, kemijskog sastava 1Cr-0,5Mo (C<0.15%, Cr0.8-1.25%, Mo0.44-0.65%). Its high-temperature strength is significantly improved through the solid solution strengthening effect of aluminum. Compared to ordinary 20G boiler tubes, its creep strength at 540°C is increased by approximately 40%, and the allowable stress can reach 78MPa (ASME standard). This material must simultaneously meet the triple standards of ASTM A335 (materials), A213 (cold drawing), and A370 (mechanical testing), and must undergo 100% eddy current testing and hydraulic testing (test pressure >60MPa) prije napuštanja tvornice.

Specifikacija

P12 čelične cijevi obično su dostupne u veličinama u rasponu od 25-762 mm u promjeru i 3-50 mm u debljini stijenke.

Ključne tehnologije u proizvodnom procesu

Proizvodnja visoko{0}}kvalitetnih SA335 P12 čeličnih cijevi zahtijeva kontrolu nad tri ključna aspekta:

1. Proces taljenja koristi trostruki postupak EAFLFVD, kontrolirajući sadržaj sumpora i fosfora na manje od ili jednako 0,015% i sadržaj vodika na manje od ili jednako 2 ppm;

2. Vruće valjanje koristi dvo-fazni kontrolirani proces valjanja, s konačnom temperaturom valjanja kontroliranom na 880±20 stupnjeva kako bi se osigurala potpuna rekristalizacija austenita;

3. Toplinska obrada mora se pridržavati režima normalizacije (900-930 stupnjeva) i temperiranja (680-730 stupnjeva), što rezultira ujednačenom temperiranom mikrostrukturom bainita.

Prijave

U superkritičnim kotlovskim jedinicama, P12 čelične cijevi se uglavnom koriste u:
Nisko{0}}temperaturni pregrijači (temperatura stijenke manja ili jednaka 450 stupnjeva)
Zaglavlja ekonomajzera
Glavni potporni sustavi parnih cijevi